304C15

2023-05-17 16:43:42 来源：钢铁之家阅读量：0

牌号	304C15
对应标准	BS 3100-1991 一般工程用铸钢件 Specification for Steel castings for general engineering purposes
归类	铸钢
性能	耐腐蚀
标签	奥氏体不锈铸钢有磁性

304C15 化学元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni
最小值	-	-	-	-	-	18	8
最大值	0.08	1.5	2	0.04	0.04	21	11

碳当量计算

304C15 机械性能

热处理或状态	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %
ST(1000°C~1100°C)	≥480	1% proof stress Rp1.0 min ≥215	≥26

A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.

1 近似对照表耐蚀铸钢（不锈钢铸件）

中国

中国台湾

日本

韩国

美国

德国

法国

俄罗斯

瑞典

英国

ISC

CNS

JIS

ASTM

UNS

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

SS₁₄

BS EN/BS

ZG07Cr19Ni9

C53048

SCS 13A

SSC 13A

CF8

J92600

GX5CrNi19-10

1.4308

Z2CN18.10M

07Х18Н9Л

2333

304C15

2 近似对照表耐蚀铸钢（不锈钢铸件）

中国		中国台湾	日本	韩国	国际标准组织	德国		法国	俄罗斯	瑞典	英国
GB	ISC	CNS	JIS	KS	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	SS₁₄	BS EN/BS
ZG07Cr19Ni9	C53048	SCS 13	SCS 13X	SSC 13	GX5CrNi19-9	GX5CrNi19-10	1.4308	Z2CN18.10M	07Х18Н9Л	2333	304C15

3 近似对照表耐蚀铸钢（不锈钢铸件）

中国	日本	美国	德国		法国	俄罗斯	英国
GB	JIS	ASTM	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	BS EN/BS
ZG0Cr18Ni9	SUS13	CF8	G-X6CrNi18 9	1.4038	Z6CN18.10M	07Х18Н9Л	304C15

4 近似对照表耐热铸钢和耐热合金铸件

中国	日本	美国		德国		法国	俄罗斯	英国
GB	JIS	ASTM	UNS	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	BS EN/BS
ZG0Cr18Ni9	SCS13	CF	J92600	G-X6CrNi18 9	1.4308	Z6CN18.10M Z6CN19.9M	07Х18Н9Л	304C15

注：本资料来源于互联网的公开资源整理，我们不保证这些资料的准确性、完整性和适用性。这些资料仅供您参考，不应用于任何商业用途或决策依据。本资料所记载的技术信息是说明产品的代表性特点和性能的参考值，对于因误用或不当使用本资料所记载的信息等而造成的损害恕难承担责任，敬请周知。